Herein, the structural, morphological, optical and electrical properties of CdO stacked layers comprising Si slabs of thickness of 100 nm are investigated. The performance of the stacked layers, which are prepared by the thermal evaporation technique under vacuum pressure of 10-5 mbar, is remarkably enhanced via insertion of Si thin slabs. The presence of Si slabs between the layers of CdO improves the crystallinity and surface morphology, increases the light absorbability in the ultraviolet and visible ranges of light and also increases the dielectric constant, the quality factor, and optical conductivity values. The optical conductivity parameters, which are analyzed in accordance with Drude-Lorentz approach, have shown that the insertion of the Si layers rises the values of the drift mobility of holes in CdO and lowers the free holes concentration. The energy band gap of CdO films is narrowed from 2.20 to 1.27 eV upon insertion of Si slabs. The applicability of the plasmonic CdO/Si/CdO devices as low pass filers in the frequency domain of 0.01-1.80 GHz is verified through impedance spectroscopy measurements.

Abstract Herein, the design and characterization of Ag/SeO2/C avalanche type resonant tunneling devices are reported. Thin pellets of SeO2 nano-powders pressed under hydraulic pressure of 1.0 MPa which is used as the active material are characterized. They showed tetragonal structure refereeing to space group of P 4 2 m b c and lattice parameters of a = b = 7.866 Å and c =5.336 Å. The current-voltage characteristic curves have shown that SeO2 can perform as active media to produce resonant tunneling diodes when forward biased and as avalanche type diode when reverse biased. The peak to valley current ratios of these diodes reached 18.3. In addition, the impedance spectroscopy measurements have shown that the device works in the low impedance mode when operated in the microwave range of frequency near 1.50 GHz. Negative conductance effect is observed in that frequency domain. The features of the Ag/SeO2/C nominate them for use as signal amplifiers and microwave oscillators.